Follow-up of zirconia crystallization on a surface modified alumina powder

Here we report how thermal treatments of a surface modified α-alumina powder on which a zirconium oxide precursor was grafted can be tailored so as to obtain an alumina-zirconia composite powder with well-controlled phase distribution and size. The transformation of the zirconia precursor from a starting amorphous phase to zirconia nano-grains bonded to the alumina particles surface was followed by X-ray diffraction (performed at room temperature on different thermally treated powders, as well as in situ at high-temperature) and by both conventional and high resolution transmission electron microscopy (TEM and HRTEM). Phase and nanostructure evolutions were followed on a large temperature span. The crystallization kinetics were analysed in terms of nucleation-growth mechanisms by exploiting Avrami-Johnson-Mehl-Kolmogorov formalism. Based on the above investigations, a tentative description of nucleation and growth features is proposed. This knowledge-based step represents a first approach towards nanopowders engineering.