UV-Cured polysiloxane epoxy coatings containing titanium dioxide as photosensitive semiconductor

UV-cured polysiloxane epoxy coatings containing titanium dioxide were prepared by means of a cationic photopolymerization process. A good distribution of the inorganic filler was achieved within the polymeric network with an average size dimension of around 500 nm. UV-vis analysis performed on organic dye (methylene blue) stained coatings showed a high efficiency of the titania photocatalytic activity: a complete degradation of the dye on the coating surface is reached after 60 min of UV irradiation without affecting the matrix photo-degradation.